E410-16

AWS A5.5 E410-16 | ASME SFA 5.5 E410-16

410 electrodes are used for welding AISI 410 straight chromium steels where good strength and ductility, as well as corrosion and oxidation resistance at temperatures as high as 1500°F is a requirement. 410 electrodes contain 12% chromium thereby producing weld deposits that are martensitic and not subject to carbide precipitation. Utilization does require preheat and postheat treatment to achieve good ductility in the welds. 410 is also used for welding AISI 403, 405, 414, 416 and 420 stainless steels, for overlaying carbon steels to provide corrosion, erosion and abrasion resistance, and as a buildup on sealing faces of gas, water and steam fittings which are made from unalloyed or low-alloyed steels

TYPICAL WIRE CHEMISTRY (%)

-

AWS SPEC

TYPICAL WELD METAL

C

0.12

0.056

Cr

11.0-13.5

12.07

Ni

0.7

0.57

Mo

0.75

0.024

Mn

1.0

0.82

Si

0.90

0.32

P

0.04

0.023

Cu

0.75

0.024

S

0.03

0.011

Typical weld metal properties

-

AWS Spec

Weld Metal

Ultimate tensile strength (psi)

75,000 min

94-109,480

Yield Strength (psi)

N/A

64-71,000

Elongation in 2" (%)

20% min

22.4%